所属单位：[1]Univ Elect Sci & Technol China, State Key Lab Elect Thin Films & Integrated D, Chengdu 610054, Peoples R China

发表刊物：JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS

关键字：hexagonal ferrite; Bi2O3; mixing; sintering behavior; microstructure; high-frequency magnetic property

摘要：Z-type hexaferrites with composition of Ba-3(Co0.4Zn0.6)(2)Fe24O41+ xwt% Bi2O3 (where x = 0-2) were prepared by a solid-state reaction method. The effects of different mixing procedures and Bi2O3 content on the sintering behavior, phase composition, microstructure and magnetic properties of the samples were investigated. It was confirmed that with the same secondary mixing time (t(2)), increasing the primary mixing time (t(1)) leads to a decrease of the average grain size and an increase of the initial density. The initial density and the distribution of particles and pores determined the sintering density. With t(1) = 24 h and t(2) = 6 h, the sintering density reached its maximum. The initial permeability and Q-factor also peaked, which could be attributed to the highest sintering density and compact microstructure. Further studies showed that with increasing Bi2O3 content, the major phase changed to the Z-phase; simultaneously, the remnants content of intermediate phase decreased. The Bi2O3 additive, as a reaction center, promoted the grain growth at lower temperatures. The decrease of the sintering temperature and the partial agglomeration of Bi2O3 on the grain boundaries restrained abnormal grain growth, thus closed pores in grains were not formed. A maximum initial permeability, a higher Q-factor, a cutoff frequency of 900 MHz and a resonance frequency above 1.8 GHz were obtained for the sample with 0.6 wt% Bi2O3 sintered at low temperature. (c) 2007 Elsevier B.V. All rights reserved.

文献类型：Article

卷号：316

期号：1

页面范围：67-72

ISSN号：0304-8853

是否译文：否